Aluminum Foil XPE Foam

Aluminum Foil XPE Foam

Aluminum foil XPE foam is a newly developed thermal and acoustic insulation material made from cross-linked polyethylene foam (XPE foam) covered with pure reinforced aluminum foil or aluminum coated film on both sides. The XPE foam as the base material has numerous characteristics of high tensile strength and tear resistance, and it is well suitable for applications requiring insulation materials with properties of thermal insulation, sound proofing, low water absorption, weather durability, chemical resistance and aging resistance. Pure aluminum foil is used as skin laminated to the XPE foam, providing reflective surface, corrosion resistance as well as good heat insulation. Our aluminum foil XPE foams are widely used as reflective insulation material for construction of industrial, commercial and residential building.

Features Strong moisture barrier, heat insulation, sound proofing, energy saving High tensile strength, superior tear resistance Lightweight, flame retardant, easy to cut and install Odorless, environmentally friendly Low thermal conductivity, excellent thermal insulation Keep building warm in winter and cool in summer Basic Information Material: XPE pure aluminum foil (or aluminum coated film) Structure: aluminum foil XPE aluminum foil/ aluminum foil IXPE aluminum foil (or customized, e.g. woven fabric aluminum foil) Foam density: 30B (33kg/m³) Dimensions: 4mm×1350mm×40mts (or customized) Thickness: single layer 3-15mm, multi-layer 15-200mm, available in self-adhesive backing on one side Flame retardant: UL94 HF-1, GB8624-B1 Color: grey, black, white Technical Data

Property		Standard	Unit	Value
Density		-	Kg/m3	33.33
Tensile strength	Transverse	ISO-1798	MPa	0.25~0.27
	Longitudinal			0.31~0.32
Elongation	Transverse	ISO-1798	%	137.40~141.20
	Longitudinal			159.70-166.00
Tearing strength	Transverse	ISO-8067	Kn/m	1.28~1.33
	Longitudinal			1.38~1.40
Compression 25%		ISO-3386-1	kPa	36.40
Compression 40%		ISO-3386-1	kPa	62.40
Compression 50%		ISO-3386-1	kPa	95.20
Compression set 25% 0.5H		ISO-1856	%	19.10
Compression set 25% 24H		ISO-1856	%	4.10
Operating temperature range		Internal	℃	(-40~ 80)
Water absorption % volume(maximum)		Internal	%	0.50
Thermal conductivity		JISA1412-2	W/mK	0.032
Shore- C		ASTM D2240	℃	22

Applications