Polyester Extrusion, Blow Molding TPU Material

The blow molding TPU material has numerous characteristics, including outstanding physical properties, excellent mechanical properties, good environmental performance, great processability, high extrusion stability, strong resistance to cold and heat, and more. It is widely used in thin film, air cushions, pipes and ultra-thin film.

Product Parameters

Product series Huafon TPU 33/34/38 series
Hardness: shore A80--shore D60
Operation: Extrusion, blow molding, film blowing
Characteristics: Outstanding physical properties, good mechanical properties, strong wear resistance, high tear strength, rapid forming performance, excellent cold and heat resistance
Main models: 3380A, 3385A, 3885A, 3390A, 3890A, 3395A, 3895A, 3398A, 3492A, 3495A, 3495AT

Technical Specifications
HF-3890AE Polyester Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3890AE	92A	35	650	150	9.5	/

HF-3895AE Polyester Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3895AE	95A/58D	38	550	190	14	/

HF-3785A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3785A	85 A	30	700	105	5.5	/

HF-3795A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3795A	95 A	26	400	190	16	/

HF-3380A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3380A	80A	25	800	100	3.5	120

HF-3385A Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3385A	87A	28	700	120	7	/

HF-3390AX Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3390AX	91A	30	650	140	8	/

HF-3395AX Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3395AX	95 A	32	500	180	14	/

HF-3398AX Polyester Extrusion Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3398AX	60D	38	350	200	17.5	100

HF-3492A Polyester Blow Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3492A	92A	45	700	150	10	/

HF-3495A-6 Polyester Blow Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3495A-6	95 A	45	600	160	12	/

HF-3495AT Polyester Blow Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm 3
HF-3495AT	95A	45	500	180	12	/

Application Examples