Mixing Blade (for Concrete Mixer)

Name: Mixing blade
Suitable for: Concrete batch plant, concrete mixers of various brands including SANY, ZOOMLION, NFLG, SICOMA, XCMG, Teka, Fangyuan, BHS, Huajian, Shaoguan, JS, etc.
Materials: High manganese steel, modified high manganese steel, alloy steel, bimetal composite material, high chromium material, ultra high chromium cast iron, multi-component alloy steel
Customizable or not: Yes
Part model: Based on customer's needs
Order quantity: Based on customer's needs

Applications
The concrete mixer replacement parts are ideal for the concrete mixers used in cement, chemical, power, metallurgy and other industries.

Samples Show Concrete mixer blades for SICOMA mixer Concrete mixer blades for SICOMA mixer Mixing blades for SANY JS3000 concrete mixer Mixing blades for HUAJIAN JS1500b, JS2000b and JS3000b concrete mixers Mixing blades for ZOOMLION JS3000 mixer

JS3000 concrete mixer mixing blades for NFLG HZS180 concrete batch plant Mixing blades for BHS2.0, BHS3.0, BHS4.5 and DKXS concrete mixers Mixing blades for ELBA1650 and ELBA60 concrete mixers Mixing blades for Nikko DSF167, DSF225, DSF275 and DSF330 concrete mixers Mixing blades for SHAOGUAN JS3000FG and JS2000FA concrete mixers

Order Information
1. Concrete Mixer Spare Parts
a. Quality standard: National Standard GB/T8263-1999 (Substitute Japanese and ASME products)
b. Supporting concrete mixers: SICOMA, BHS, YKYC, TEKA, SANY, NFLG, FYG, DG; AMMANN, NIKKO, ACP, MARINI; ABG, VOEGELE, DEMAG, DYNAPAC, XCMG
c. Metallographic organization: M M7C3 M23C6
d. Shock toughness: 6-8 J/cm2

2. Technical Specifications

Hardness	52-62HRC
Life	More than 200,000 cubic meter concrete or 300,000 tons asphalt
Standards	CN:KM TB Cr 15-25-GTUS:ASTM A532 Class Two Type D
Extension strength	380 N/mm2
Elongation at break	1%
Shock impact (resistance) value	>5 ak N.M/CM2
Flexural strength	>600 ak N.M/CM2
Certifications	ISO9001:2008,
Metallographic organization	M M7C3 M23C6
Process	Lost Foam Casting

3. Chemical Compositions

Name	Chemical Compositions %									Hardness
	C	P	S	Si	Mn	Cr	Ni	Mo	Cu
Special high chrome steel	2.8~3.1	<0.06	<0.06	0.8	0.8	22	<1	<1	<0.5	62
High chrome steel	2.8~3.1	<0.06	<0.06	0.8	0.8	15		<0.5		52
Low chrome steel	2.8~3.1	<0.06	<0.06	0.8	0.8	3				48
High manganese steel	1.2	<0.06	<0.06		16					45
Alloy steel casting	1.2	<0.06	<0.06		2	1				45