Hot Dip Galvanized Iron Wire

Send Message Request a Quote

Hot Dip Galvanized Iron Wire

We at Wanlida are a hot dip galvanized iron wire manufacturer in China, with a production capacity of more than 2,000 tons per month. Our hot dip galvanized iron wire is one of our primary products. Made using low carbon steel wire and through wire drawing, acid washing, annealing and hot dip galvanizing processes, the iron wire is soft, flexible, durable and rust resistant, making it the perfect material for producing galvanized barbed wire, chain link wire mesh, gabion wire mesh, welded wire mesh, and more. As a result of its reliable quality and competitive price, Wanlida hot dip galvanized iron wire is widely used in the fields of construction, handicrafts, expressway wire mesh fence, product packaging, etc., and is increasingly popular with customers in Western Europe, North America, Latin America, Southeast Asia, the Middle East, among other countries and regions.

Specifications of Hot Dip Galvanized Iron Wire
Yield strength: 195~235Mpa
Tensile strength: 295~540Mpa or 350~680N/MM2
Elongation rate: 18~25%
Wire diameter error: ≤0.3mm ±0.02mm ＞0.3~1.6mm ±0.04mm ＞1.6~5.0mm ±0.05mm
Zinc content: first grade 200~250g/m2, second grade 150~200g/m2, third grade 40~90g/m2

Standards of Galvanized Iron Wire

Wire gauge	SWG(mm)	BWG(mm)	GB(mm)
8	4.06	4.19	4.00
9	3.66	3.76	-
10	3.25	3.40	3.50
11	2.95	3.05	3.00
12	2.64	2.77	2.80
13	2.34	2.41	2.50
14	2.03	2.11	-
15	1.83	1.83	1.80
16	1.63	1.65	1.65
17	1.42	1.47	1.40
18	1.22	1.25	1.20
19	1.02	1.07	1.00
20	0.91	0.89	0.90
21	0.81	0.813	0.80
22	0.71	0.711	0.70
23-37# galvanized iron wire can also be produced.

Material
Wire rod from large steelworks, including Q195, Q235, SAE1006/1008, etc.

Chemical Composition of Q195 Wire Rod

Type	Grade	Chemical composition (%)
		C	Mn	Si	S	P
				≤
Q195	Ⅰ	0.06~0.12	0.25~0.50	0.30	0.050	0.045

Mechanical Property of Q195 Wire Rod

Type	Tensile strength Mpa	Yield strength MPa	Elongation rate %
Q195	315~430	195	33

Chemical Composition and Mechanical Property of Q235 Wire Rod

Country	China	Type	Q235-		UNS		Standard Number	GB 700-88
Chemical composition (%)	0.14-0.22C,0.30-0.65Mn(the upper limit of Mn: 0.60),0.30Si,0.050S,0.045P, residual chromium, nickel, copper: respectively, 0.30
Shape	Ingot, blank, profile, bar, plate, tube, strip line						Process	Hot(cold) rolling, normalizing
Tensile strength Mpa	375-460			Yield strength Mpa		185-235	Elongation rate %	21-26(based on varied sizes)

Packaging of Hot Dip Galvanized Iron Wire
Package: roll, reel
Coil/reel weight: 1) 400~600kg
                          2) 200kg, 100kg, 50kg, 25kg
                          3) 10kg, or 2-8kg
Seaworthy packing:1) wrapped with plastic cloth inside, plastic woven bag outside
                              2) wrapped with plastic cloth inside, plastic Hessian cloth outside
                              3) Specific packaging requests are also accommodated, like bundling, etc.

Wanlida is a professional hot dip galvanized iron wire manufacturer located in China. In addition to hot dip galvanized iron wire, we also produce crimped stainless steel wire mesh, fiberglass window screen, stainless steel expanded mesh, and so on.