Galvanized Iron Wire
Galvanized Iron Wire
Wanlida galvanized iron wire is a metal composite material that is made with superior mild steel wire rod, through wire drawing, annealing, acid cleaning and galvanizing processes. With the features of being economical, soft, clean, easy to process and bind, the galvanized iron wire becomes the ideal building material and hardware material in Southeast Asia, Africa, South America, etc.
Applications
Wanlida galvanized iron wire is mainly used in making chain link fence, barbed wire, gabion basket, hexagonal wire netting, crimped wire mesh, expressway wire mesh fence, and more. In addition, the galvanized iron wire can also be used as binding wire to bind everyday objects.
Specifications of Galvanized Iron Wire
Yield strength: 195~235Mpa
Tensile strength: 295~540Mpa or 350~680N/MM2
Elongation rate: 18~25%
Wire diameter error: ≤0.3mm ±0.02mm ＞0.3~1.6mm ±0.04mm ＞1,6~5.0mm ±0.05mm
Zinc content: first grade 18~30g/m2, second grade 12~18g/m2, third grade 9~12g/m2
Standards of Galvanized Iron Wire
| Wire gauge | SWG(mm) | BWG(mm) | mm |
| 8 | 4.06 | 4.19 | 4.00 |
| 9 | 3.66 | 3.76 | - |
| 10 | 3.25 | 3.40 | 3.50 |
| 11 | 2.95 | 3.05 | 3.00 |
| 12 | 2.64 | 2.77 | 2.80 |
| 13 | 2.34 | 2.41 | 2.50 |
| 14 | 2.03 | 2.11 | - |
| 15 | 1.83 | 1.83 | 1.80 |
| 16 | 1.63 | 1.65 | 1.65 |
| 17 | 1.42 | 1.47 | 1.40 |
| 18 | 1.22 | 1.25 | 1.20 |
| 19 | 1.02 | 1.07 | 1.00 |
| 20 | 0.91 | 0.89 | 0.90 |
| 21 | 0.81 | 0.813 | 0.80 |
| 22 | 0.71 | 0.711 | 0.70 |
| 23 | 0.61 | 0.63 | 0.60 |
| 24 | 0.56 | 0.56 | 0.55 |
| 25 | 0.51 | 0.50 | 0.50 |
| 26 | 0.46 | 0.45 | 0.45 |
Material
Wire rod from large steelworks, including Q195, Q235, SAE1006/1008, etc.
Chemical Composition of Q195 Wire Rod
| Type | Grade | Chemical composition (%) | ||||
| C | Mn | Si | S | P | ||
| ≤ | ||||||
| Q195 | Ⅰ | 0.06~0.12 | 0.25~0.50 | 0.30 | 0.050 | 0.045 |
Mechanical Property of Q195 Wire Rod
| Type | Tensile strength Mpa | Yield strength MPa | Elongation rate % |
| Q195 | 315~430 | 195 | 33 |
Chemical Composition and Mechanical Property of Q235 Wire Rod
| Country | China | Type | Q235- | UNS | Standard Number | GB 700-88 | |||
| Chemical composition (%) | 0.14-0.22C,0.30-0.65Mn(the upper limit of Mn: 0.60),0.30Si,0.050S,0.045P, residual chromium, nickel, copper: respectively, 0.30 | ||||||||
| Shape | Ingot, blank, profile, bar, plate, tube, strip line | Process | Hot(cold) rolling, normalizing | ||||||
| Tensile strength Mpa | 375-460 | Yield strength Mpa | 185-235 | Elongation rate % | 21-26(based on varied sizes) | ||||
Packaging of Galvanized Iron Wire
Package: roll, reel
Coil/reel weight: 200kg, 100kg, 50kg, 25kg(usually), 10kg, or 2-8kg
Seaworthy packing: wrapped with plastic cloth inside, plastic woven bag outside
wrapped with plastic cloth inside, plastic Hessian cloth outside
Specific packaging requests are also accommodated, like bundling, etc.
As a China based primary galvanized iron wire manufacturer, Wanlida can provide our worldwide customers with superior quality crimped stainless steel wire mesh, hexagonal wire netting, stainless steel expanded mesh, brass expanded mesh, and more.
If you are in need of our steel wire, please do not hesitate to contact us. We are happy to help you.