Halogen-free Modified Polyolefin Heat Shrinkable Tubing

Halogen-free Modified Polyolefin Heat Shrinkable Tubing, RSFR-MT-LWA-105H Medical grade heat shrink tubing Model: RSFR-MT-LWA-105H

RSFR-MT-LWA-105H halogen-free modified polyolefin heat shrinkable tubing is designed for process assistance in minimally invasive medical devices. The homogeneous structure contributes to the consistency and high performance of the medical grade heat shrink tubing, making it essentially free from defects, pinholes, seams, cracks or flaws.
This halogen-free modified polyolefin heat shrinkable tubing is provided with a customizable shrink rate (up to 4:1). Our MT-LWA-105H heat shrinkable tube has unique properties that allow it to be easily removed when heated over a specific temperature, making it an optimal alternative to FEP heat shrink tubes.

Features Shrink rate: ＞2:1 Operating temperature: -40°C ~ 105°C Initial shrink temperature: ≥ 90℃ Superior electrical insulation Compliant with ISO 10993-1 Easy to be removed after application, good axial tear expansion No heavy metals Environmental standard: RoHS compliant Standard color: transparent Properties

Performance	Test standard	Standard Performance
Longitudinal change rate (%)	ASTM D 2671	-10~ 5
Tensile strength (MPa)	ASTM D 2671	≥10.4
Elongation at break (%)	ASTM D 2671	≥200
Cold bending (-30℃, 1h)	ASM-DTL-23053	No cracks
Withstand voltage	UL224	4000V,1min, no breakdown
Volume resistivity (Ω.cm)	IEC 60093	≥1015

Size Chart(2:1 Table)

Part No.	As Supplied I.D (mm)	Recovered Size
		Inside Diameter, Max (d)	Wall Thickness (W)
		(mm)	(mm)
RSFR-MT-LWA-0.8	1.02±0.13	≤0.35	0.28±0.05
RSFR-MT-LWA-1.2	1.40±0.13	≤0.50	0.41±0.08
RSFR-MT-LWA-1.6	1.83±0.13	≤0.70	0.51±0.08
RSFR-MT-LWA-2.4	2.72±0.20	≤1.05	0.51±0.08
RSFR-MT-LWA-3.2	3.56±0.25	≤1.45	0.51±0.08
RSFR-MT-LWA-4.8	5.21±0.25	≤2.20	0.51±0.08
RSFR-MT-LWA-6.4	6.99±0.38	≤3.00	0.64±0.08
RSFR-MT-LWA-9.5	10.54±0.51	≤4.30	0.64±0.08