Introduction:
The expansion coefficient and curie point of this FeNi42 thermal expansion alloy increase with the increase of nickel content. This alloy is widely used in electric vacuum industry as sealing structure material.
Supply of thermal expansion alloy Style | Size |
Wire | D=0.1~8mm | |
Strip | W= 5~250mm | T= 0.1mm | |
Foil | W= 10~100mm | T= 0.01~0.1mm | |
Rod | D=8~100mm | L=50~1000mm | |
Chemical composition (%) Ni | 41.5~42.5 | Fe | Bal. | Co | - | Si | ≤0.3 |
Mo | - | Cu | - | Cr | - | Mn | ≤0.8 |
C | ≤0.05 | P | ≤0.02 | S | ≤0.02 | Al | ≤0.1 |
Physical property Density (g/cm3) | 8.12 |
Resistivity under 20℃(Ωmm2/m) | 0.61 |
Thermal conductivity, λ/ W/(m*℃) | 14.6 |
Curie point, Tc/ ℃ | 360 |
Elasticity modulus, E/ Gpa | 147 |
Expansion coefficient θ/℃ | α1/10-6℃-1 | θ/℃ | α1/10-6℃-1 |
20~100 | 5.6 | 20~400 | 5.9 |
20~200 | 4.9 | 20~450 | 6.9 |
20~300 | 4.8 | 20~500 | 7.8 |
20~350 | 4.95 | 20~600 | 9.2 |
Mechanical property Tensile Strength (Mpa) | Elongation (%) |
490 | 35 |
Heat treatment process Annealing | Be heated to 900 ±20℃ in hydrogen environment. |
Heat preservation (h) | 1h |
Cooling | Be cooled below 200℃ at a speed of no more than 5 ℃ / min. |