E81T5-B2C Low Alloy Steel Flux Cored Wire

Send Message Request a Quote

The E81T5-B2C low alloy steel flux cored wire is formulated with basic type slag system. This gas shielded wire is born with outstanding weldability and mechanical properties. Our low alloy steel welding equipment delivers reliable arc, negligible spatter and prime finish.

200-300℃ preheat is required by this low alloy steel flux cored wire. This welding consumable is greatly applicable for 1.0%Cr-0.5%Mo low alloy steel structures below 520℃.

Standards
GB/T17493-2008 E550T5-B2
AWS A5.29 E80T5-B2C

Chemical composition of deposited metal (%)

	C	Mn	Si	Cr	Mo	S	P
Standard	≤0.12	≤1.25	≤0.80	1.00-1.50	0.40-0.65	≤0.030	≤0.030
Typical	0.08	0.85	0.31	1.20	0.45	0.010	0.018

Mechanical properties of deposited metal(620℃ × 1h)

	Rm (MPa)	Rp0.2 (MPa)	A5 (%)
Standard	550-690	≥470	≥19
Typical	618	535	22

Recommended welding data (DC , shielding gas: CO2)

Wire diameter (mm)	Current (A)	Voltage (V)	Gas (l/min)
Φ1.2	200-260	24-30	15-20
Φ1.6	220-280	24-32	15-20